Superwide Aluminium Micro channel Pipe for Heat Exchanger
1.Application of aluminum micro pipe:
|No.||Alloy||Temper||Tensile Strength(Mpa)||Yield Strength(Mpa)||Elogation(%)|
|1||1050||O/F/H111/H112||≥ 65||≥ 20||≥ 25|
|2||1100||O/F/H111/H112||≥ 75||≥ 20||≥ 25|
|3||1197||O/F/H111/H112||≥ 80||≥ 25||≥ 20|
|4||3102||O/F/H111/H112||≥ 75||≥ 20||≥ 25|
|5||3R03||O/F/H111/H112||≥ 80||≥ 25||≥ 20|
5.Chemical Composition for Aluminum Micro channel Tube
|1||1050||≤ 0.25||≤ 0.40||≤ 0.05||≤ 0.05||≤ 0.05||-||≤ 0.05||≤ 0.05||≤ 0.03|
|2||1100||≤ 0.95(Fe+Si)||0.05-0.20||≤ 0.05||-||-||≤ 0.10||-||-|
|3||1197||≤ 0.15||≤ 0.20||0.40-0.55||0.10-0.20||≤ 0.03||≤ 0.05||≤ 0.05||≤ 0.05||≤ 0.05|
|4||3102||≤ 0.40||≤ 0.70||≤ 0.10||0.05-0.40||-||-||≤ 0.30||-||≤ 0.10|
|5||3R03||≤ 0.15||≤ 0.15||≤ 0.01||0.90-1.10||≤ 0.03||≤ 0.03||≤ 0.05||≤ 0.05||≤ 0.05|
6. Size Tolerance
|Width||Thickness||Wall Thickness||Length||Lateral Curvature||Frontal Curvature||Twsiting Dgree|
|± 0.05mm||± 0.03mm||± 0.05mm||± 0.03mm||≤ L× 0.2%||≤ L× 0.25%||≤ L× 0.15%|
7.Our products will be tested in strict standard before delivery, some data for your reference.
|No||Products' Testing Name||Contents and requests|
|1||Corrosion Resistance||Salt spray test: ≥ 750 hours|
|2||Zn Coating Standards||6/8/10/13± 2g/square meter|
|3||Flux Cotaing Standards||10-15± 2g/square meter|
|Minimum Order Quantity:||5 metric tons|
|Payment Terms:||T/T or LC|
|Supply Ability:||50,000 mt per year|
|Delivery Time:||30 working days after received your down payment|
|Packaging Details:||Standard export packaging|
Trumony Aluminum Co.LTD build from 2006, have export over 53 countries of worldwide. Our main products are aluminum alloy cladding material, cole material and other aluminum products like aluminum sheet, aluminum plate, aluminum coil, aluminum foil, 6101 T63 High Conductivity Aluminum Conduction Plates, aluminum strip, aluminum pipe, Oil Cooler Tube，aluminum tube, aluminum heat exchange etc, for automobile heat exchangers area such as radiator, intercooler, condenser, evaporator and industrial heat exchangers, like electricity power radiator, air conditioner etc.There are complete sets of modern production and testing equipment operation workshops for casting, hot rolling, cold rolling, coating finishing and advanced check-out for researching and testing,such as WDW-3010- micro-controlled electronic universal testing machine,CALS-2000 aluminum alloy metallographic image analysis system etc.
1, Q: Are you manufacturer?
A: Yes, we are established in 2003. As a manufacturer our customers are welcome to visit our factory.
2, Q: Do you accept customized orders?
A: Yes, we do. Your customized orders are always welcomed. Please kindly offer us your technical perfrmances or samples so that we can customize the products according to your preferences. About any further detail, please feel free to contact us.
3. Q: How can I get one quotation faster?
A: Pls offer details about your demands as more as possible,insulation thickness,over diameter,nominal voltage,working temperature,color,quantity,application,etc.
4. Q: If I can not offer above information,what should I do?
A: Try your best to offer more information,we will help you design suitable wires&cables.
5. Q: What is your company sample policy?
A: As one supplier,we see that sample is necessary for our both sides,our policy is to offer free sample as possible as we can,just one situation is exception,sample is with very complex structure,besides,we have no it in stock.
About sample shippment,you need to pay for the freight,usually freight collect by express.
6. Q: What is the lead time of sample?
A: There are several different situations:
Immediately when you need it if we have it in stock;
1~2days if no stocked sample and the sample structure is not complex;
3~5days if no stocked sample and the sample is with complex structure.